graphene을 300배의 THF에 분산한 후 30분간 son

graphene을 300배의 THF에 분산한 후 30분간 sonication 하였다. 고분자를 8배의 THF에 녹인 후, 위의 graphene 분산액과 섞은 후, 200 rpm의 교반기로 24 시간 혼합하였다. 추가적으로 교반하면서 대부분의 용매를 날린 후, 60 ℃에서 24 시간 건조하였다. 건조된 시료를 225 ℃, 9.8 MPa의 압력 조건에서 압축성형하여 sheet 형태로 만들었다

결과 (영어) 1:

After you have distributed to 300 times the graphene THF sonication for 30 minutes. 8 times the polymers melt in THF, then the above 200 rpm, then mixed with dispersant and graphene's agitator with a 24-hour mix. In addition, most of the solvents with stirring after 60 ° c dry 24 hours flown. Dry the sample to 225 ° c, 9.8 MPa of pressure in terms of compression molding made in the form of a sheet

결과 (영어) 2:

After the dispersion of graphene in THF was 300 times sonication 30 minutes. Dissolved the polymer in an 8-fold THF, was mixed with graphene dispersions of the above, it was mixed for 24 hours on a 200 rpm stirrer. After putting them most of the solvent, while stirring further, and it dried 24 hours at 60 ℃. The dried sample ℃ 225, made in sheet form by compression molding at a pressure of 9.8 MPa conditions

결과 (영어) 3:

three hundred and THF graphene scattered in the sonication, for 30 minutes. the THF, eight times in the graphene melted, mixed and dispersed liquid after 24 hours of 200 rpm mixer for mixing. additional, the stirring of the every day, after 24 hours, 60 degrees in the dry. it is a group of data 225 degrees, pressure of molding conditions 9.8 MPa in sheet form, is made.